[AR] Re: Vacuum processing of solid propellant

  • From: "Anthony Cesaroni" <anthony@xxxxxxxxxxx>
  • To: <arocket@xxxxxxxxxxxxx>
  • Date: Sun, 7 Jul 2019 14:43:25 -0400

Discharge machine extra.:-)

 

 



 

 

Anthony J. Cesaroni

President/CEO

Cesaroni Technology/Cesaroni Aerospace

 <http://www.cesaronitech.com/> http://www.cesaronitech.com/

(941) 360-3100 x101 Sarasota

(905) 887-2370 x222 Toronto

 

 

From: arocket-bounce@xxxxxxxxxxxxx <arocket-bounce@xxxxxxxxxxxxx> On Behalf
Of William Claybaugh
Sent: Sunday, July 7, 2019 12:40 PM
To: arocket@xxxxxxxxxxxxx
Subject: [AR] Vacuum processing of solid propellant

 

I ran some static tests recently using a modified version of the standard
RRS composite propellant (10% Al rather than 7%).  Those tests included
applying vacuum to the fully processed mix ahead of casting (5 minutes); the
mix was still outgassing when we repressurized

 

This resulted in an about 5.6 % increase in density, of which 0.9% is
attributable to the increased Al loading.

 

Given that full mixing under vacuum is not viable given the processing
equipment available at the MTA, is there another vacuum schedule that might
provide still higher density?

 

Does degassing the liquid components before mixing help or does the
subsequent mixing just reintroduce air?  Any recommendations on degassing
time after mixing (recognizing that the catalyst is in the mix at this
point).

 

Two static tests, one at 390 psia average and the other at 760 psia average
showed a decreased burn rate and a slightly higher ISP as compared to the
original mix, as expected.

 

Bill 

JPEG image