[AR] Re: Vacuum processing of solid propellant

  • From: "Troy Prideaux" <troy@xxxxxxxxxxxxxxxxxxxxx>
  • To: <arocket@xxxxxxxxxxxxx>
  • Date: Mon, 8 Jul 2019 10:01:31 +1000

Yup, that’s the dump (actually casting) valve. So the ball’s stem (it’s a ball 
valve) is loosely coupled to an o-ring sealed sleeve with the handle attached 
through the outer stainless steel casing/jacket that allows vacuum operation of 
the valve; which allows the casting whilst still under vac & while even the 
mixing paddle is still rotating. As illustrated this can be removed to enabled 
the main mixing hopper to be removed for cleaning or whatever.

 

BTW: what’s not illustrated there is a paddle height control at the very top of 
the main spindle shaft. This allows for adjustment of mixing paddle during 
operation (under vac mixing). This is a *really* useful function for different 
mix viscosities allowing me to strike the right balance (stuff sticking to 
paddle vs sticking to mixing hopper) for very small mixes and it also helps to 
minimise wastage as I can set it low enough to virtually scape the hopper at 
the end to ensure just about everything is transferring into the casting 
tube(s).

 

Troy

 

From: arocket-bounce@xxxxxxxxxxxxx [mailto:arocket-bounce@xxxxxxxxxxxxx] On ;
Behalf Of anthony@xxxxxxxxxxx
Sent: Monday, 8 July 2019 9:35 AM
To: arocket@xxxxxxxxxxxxx
Subject: [AR] Re: Vacuum processing of solid propellant

 

Well done. Is that a valve at the bottom of the bowl?

 

Anthony J. Cesaroni

President/CEO

Cesaroni Technology/Cesaroni Aerospace

 <http://www.cesaronitech.com/> http://www.cesaronitech.com/

(941) 360-3100 x101 Sarasota

(905) 887-2370 x222 Toronto

 

From: arocket-bounce@xxxxxxxxxxxxx <mailto:arocket-bounce@xxxxxxxxxxxxx>  
<arocket-bounce@xxxxxxxxxxxxx <mailto:arocket-bounce@xxxxxxxxxxxxx> > On Behalf 
Of Troy Prideaux
Sent: Sunday, July 7, 2019 7:26 PM
To: arocket@xxxxxxxxxxxxx <mailto:arocket@xxxxxxxxxxxxx> 
Subject: [AR] Re: Vacuum processing of solid propellant

 

No, it’s a totally custom made contraption 
http://www.propulsionlabs.com.au/mixer/

 

Mixes and casts under vac with optional dry gas purge/re-pressurizing at the 
end.

 

Cheers,

 

Troy

 

 

From: arocket-bounce@xxxxxxxxxxxxx <mailto:arocket-bounce@xxxxxxxxxxxxx>  
[mailto:arocket-bounce@xxxxxxxxxxxxx] On Behalf Of William Claybaugh
Sent: Monday, 8 July 2019 8:57 AM
To: arocket@xxxxxxxxxxxxx <mailto:arocket@xxxxxxxxxxxxx> 
Subject: [AR] Re: Vacuum processing of solid propellant

 

Troy:

 

What mixer do you use under vacuum?  Is it modified for this use or did you 
find one? If modified, what did you do to it?

 

Bill

 

On Sun, Jul 7, 2019 at 4:53 PM Troy Prideaux <troy@xxxxxxxxxxxxxxxxxxxxx 
<mailto:troy@xxxxxxxxxxxxxxxxxxxxx> > wrote:

This is why I do all my mixing and casting under vac. Normally NCO will favour 
H2O over OH in terms of reactivity although OH groups do some in various 
different reactivities.


Troy

 

From: arocket-bounce@xxxxxxxxxxxxx <mailto:arocket-bounce@xxxxxxxxxxxxx>  
[mailto:arocket-bounce@xxxxxxxxxxxxx ;<mailto:arocket-bounce@xxxxxxxxxxxxx> ] On 
Behalf Of 1bcjolly
Sent: Monday, 8 July 2019 5:09 AM
To: arocket@xxxxxxxxxxxxx <mailto:arocket@xxxxxxxxxxxxx> 
Subject: [AR] Re: Vacuum processing of solid propellant

 

Some suggestions:

 

1)  Do you dry your AP?  I have found that AP contains moisture, supposedly 
from absorption from the atmosphere.  This water can be driven off by drying at 
a temperature of 240 F.  Drying the AP before mixing should also help the cure 
if you are using OH/NCO chemistry since moisture  contamination uses up NCO 
functional groups.

 

2)  Use slow mix speed.  Baking type mixers on almost any speed will introduce 
air into the mix.  

 

Barry C 

 

 

 

Sent from my Sprint Tablet.

 

-------- Original message --------

From: Anthony Cesaroni <anthony@xxxxxxxxxxx <mailto:anthony@xxxxxxxxxxx> > 

Date: 7/7/19 14:43 (GMT-05:00) 

To: arocket@xxxxxxxxxxxxx <mailto:arocket@xxxxxxxxxxxxx>  

Subject: [AR] Re: Vacuum processing of solid propellant 

 

Discharge machine extra.:-)

 

 



 

 

Anthony J. Cesaroni

President/CEO

Cesaroni Technology/Cesaroni Aerospace

 <http://www.cesaronitech.com/> http://www.cesaronitech.com/

(941) 360-3100 x101 Sarasota

(905) 887-2370 x222 Toronto

 

 

From: arocket-bounce@xxxxxxxxxxxxx <mailto:arocket-bounce@xxxxxxxxxxxxx>  
<arocket-bounce@xxxxxxxxxxxxx <mailto:arocket-bounce@xxxxxxxxxxxxx> > On Behalf 
Of William Claybaugh
Sent: Sunday, July 7, 2019 12:40 PM
To: arocket@xxxxxxxxxxxxx <mailto:arocket@xxxxxxxxxxxxx> 
Subject: [AR] Vacuum processing of solid propellant

 

I ran some static tests recently using a modified version of the standard RRS 
composite propellant (10% Al rather than 7%).  Those tests included applying 
vacuum to the fully processed mix ahead of casting (5 minutes); the mix was 
still outgassing when we repressurized

 

This resulted in an about 5.6 % increase in density, of which 0.9% is 
attributable to the increased Al loading.

 

Given that full mixing under vacuum is not viable given the processing 
equipment available at the MTA, is there another vacuum schedule that might 
provide still higher density?

 

Does degassing the liquid components before mixing help or does the subsequent 
mixing just reintroduce air?  Any recommendations on degassing time after 
mixing (recognizing that the catalyst is in the mix at this point).

 

Two static tests, one at 390 psia average and the other at 760 psia average 
showed a decreased burn rate and a slightly higher ISP as compared to the 
original mix, as expected.

 

Bill 